Ferro Silicon Magnesium
|
Brand/Марка |
Chemical composition / Химический состав(%) |
||||||
|
Mg |
Re |
Si |
Ca |
Al |
Ti |
Fe |
|
|
FeSiMg5Re2 |
4.0-6.0 |
1.0-3.0 |
38-44 |
2.0-3.0 |
<1.0 |
<0.5 |
balance |
|
FeSiMg6Re1 |
5.0-7.0 |
0.5-1.5 |
38-44 |
2.0-3.0 |
<1.0 |
<0.5 |
balance |
|
FeSiMg7Re1 |
6.0-8.0 |
0.5-1.5 |
38-44 |
1.0-1.5 |
<1.0 |
<0.5 |
balance |
|
FeSiMg7Re3 |
6.0-8.0 |
2.0-4.0 |
38-44 |
2.0-3.5 |
<1.0 |
<0.5 |
balance |
|
FeSiMg8Re3 |
7.0-9.0 |
2.0-4.0 |
38-44 |
2.0-3.5 |
<1.0 |
<0.5 |
balance |
|
FeSiMg8Re5 |
7.0-9.0 |
4.0-6.0 |
38-44 |
2.0-3.5 |
<1.0 |
<0.5 |
balance |
|
FeSiMg8Re7 |
7.0-9.0 |
6.0-8.0 |
38-44 |
2.0-3.5 |
<1.0 |
<0.5 |
balance |
|
FeSiMg10Re7 |
9.0-11.0 |
6.0-8.0 |
38-44 |
2.0-3.5 |
<1.0 |
<0.5 |
balance |
|
FeSiMg25Si40 |
25-40 |
1.5-2.0 |
40-45 |
1.5-3.0 |
<1.0 |
<0.5 |
balance |
Application:
1,For modifying castings of high-strength cast iron
2, Ferro Silicon Magnesium is the most economical addition reagent for introducing magnesium into the melt when smelting high-strength cast iron. It can reduce the cost of modification.
3, Increasing the uniformity of the castings structure, reducing gas release due to the introduction of elements, such as Ca and Ba.
4, Increasing the amount of spherical graphite and improve its structure by adding well-balanced components-Mg, Ca, Re.
5, FeSiMg is currently the most widely used modifier in the production of high-strength cast iron .
Size: 10-50mm or other.
Packing:In big bags.